TAB series of high alcohol resistant&high wear resistant single component coatings

Product description: TA series has good adhesion and excellent construction.
Main components: Thermoplastic acrylic resins, pigments, auxiliaries, organic solvents.
Applicable products: It is suitable for household appliances, life electric appliance, 3C electronic products, etc.
Applicable base materials: ABS﹑PS﹑HIPS﹑PC etc.
Environmental conformance: Meet the requirements of ROHS. Can also be designed the products according to customer requirements to meet Reach/PAHS/ halogen-free /EN71-3 etc.

Workpiece inspection  -->  degreasing and dedusting --> Confirmation of the furnace temperature --> painting --> inspection --> packaging for good products

Construction conditions：

Name	TAB series of high alcohol resistant&high wear resistant single component coatings
Blending water	W-TA series blending water
Blending percentage	paint: blending water= 1:1.5-2.5(Depending on the customers construction technology and work piece)
Construction viscosity	9-11S(NK#2/25±1℃)
Spray gun caliber	1.0-1.5mm
Spray gun pressure	3-5Kg/cm2
Spray distance	15-20cm
Thickness of dry film	8-13μm
Construction environment	temperature: 5-40℃/ humidity: 40-80%
Dry condition	room temperature×5～10mins
Baking condition	65±5℃×30

性能：

Test project		Test Method	Test result
Adhesion		Cross-cut test, 3M600 tape stripping test	5B
Hardness		MITSUBISHI UNI diurnal pencil, carry weight 500gf, ∠45°	≥HB
Alcohol resistance		99.7% alcohol, carry weight 500gf, frequency:40times(come and go)/mins	≥200 times
		Bottom materials invisiable
Heat and humidity resistance		40℃×90%RH×120H	No obvious change in the surface of the paint film
Thermal cycling		(-20℃×2H-room temperature×1H-60℃×2H-room temperature×1H)	No obvious change in the surface of the paint film
		10 times cycling

1﹑Please stir well before use；

2﹑Please refer to "construction technology instruction" to remove oil, degrease and dust before use；

3﹑Please use the suitable strainer screen for filtration;

4﹑For performance testing, please bake at 65±5℃×2H condition and process after cooling for 30 minutes；

5﹑Due to the different types and forming conditions of the rubber, please confirm it fully before using the coating to ensure its adaptability；

6﹑When the humidity is too high, besides adding the necessary anti white solvent, it is suggested that put into the bake road or oven to prevent blushing；

7﹑The coating should not be too thin and too thick, too thin to protect the film, it is easy to affect the chemical resistance test when coating again if it is too thick；

Warm reminder

Quality guarantee period: The expiration date is half a year with sealed。

Storage conditions: Stored in a cool, dry, special chemical reservoir, away from the fire source。